德路 AD224
描述信息
http://pdf.bondme.com//files/product/2017/07/06/bf/Pzkgj.pdf
产品应用
- - for the fast, high-strength bonding of components and assembly groups
- - fast curing at moderate temperatures
- - very good adhesion to LCP, reflow consistent
- - the cured product is normally used in a temperature range of -40 °C to +150 °C
- depending on the application, other limits may be more reasonable
- - compliant with RoHS directive 2015/863/EU
技术性能
密度/比重Density/specific gravity
1.2 g/cm^3
产品形态Product form
液态Liquid
玻璃化转变温度Glass transition temperature
80 ℃
颜色Color
black
固化方式Cure Method
Heat
ROHS认证ROHS compliant
YES
材料体系chemical system
Epoxy base
邵氏硬度Shore Hardness
75 D
化学类型Chemical type
Epoxy
吸水率Water Absorption
0.6 %
粘度viscosity
25000 mPa·s mPa·s
转速speed
10 r/sec r/sec
测试温度test temperature
23 ℃ ℃
剪切力Shear
26 Mpa Mpa
基材Substrate
Al
制样固化温度sample cure temperature
120 ℃ ℃
制样固化时间sample cure time
15 min min
胶层厚度Bonding line thickness
1.6 mm mm
表面状态Surface condition
sand-blasted
类型type
线性
热膨胀率thermal expansion ratio
108 ppm/K ppm/K
Tg标准Tg level
小于Tg
温度temperature
90 ℃ ℃
固化时间cure time
60 min min
有效期Shelf life
6 Month Month
存储条件Storage
in unopened original container;@-18°C
条件Conduction
长期低温
工作温度Operating/Working Temperature
-40 ℃ ℃
强度类型Strength Item
断裂强度
强度值/模量值Strength Value
22 MPa MPa
延伸率elongation
12 % %
收缩率Shrinkage
2.7 % %
类型Type
体积收缩
基材substrate
Al
压缩剪切强度compressive shear strength
48 Mpa Mpa
——改性环氧树脂
-单组分，热固化，无溶剂，无填充，触变